it is a three-layer flexible composite material, produced by using H-class adhesive to adhere the two sides of polyimide film with alkali-free glass cloth. It is with good physical mechanical property, dielectric property, soft and tear resistant, heat property and fire resistance property.
-Good mechanical, electric, thermal properties.
-Thermal class is H (180 C).
-Used instead of Nomex paper and Nomex paper laminates
-Used as layer insulation of class H and F dry type transformer.
-Slot insulation,
-Pas insulation.
-Turn- to- turn insulation in electric motors.
-Marks: we can make thickness 0.1mm - 0.4mm
1. Temperature F/H class
2. Excellent heat resistance, dielectric properties and mechanical strength.
3. Good cutting resistance, overload resistance, high rigidity, good compatibility with insulating paint
4. The slots, turns and linings of F-class motors and appliances are insulated.
5. Form: roll, sheet, strip
| No. | Name | Unit | Value | |||
| 1 | Thickness | mm | 0.2 | |||
| 2 | Melting point | ºC | non-fusible | |||
| 3 | Dimensional stability at high temperature | 150ºC | ≤0.35 | |||
| 400ºC | ≤2.50 | |||||
| 4 | Tensile strength | MD | no bending | N/10mm | ≥330 | |
| After bending | ≥290 | |||||
| CD | no bending | ≥310 | ||||
| After bending | ≥270 | |||||
| 5 | Volume resistivity | Ω·m | ≥1.0×1010 | |||
| 6 | Breakdown Voltage | No bending | KV | 15 | ||
| After bending | 13 | |||||
| 7 | Elongation at break | MD, no bending | % | ≥50 | ||
| CD, no bending | ≥50 | |||||
| 8 | alternating current electric strength | No bending | KV | ≥25 | ||
| After bending | ≥23 | |||||
| 9 | Long time thermostability,Insulation Class | / | ºC | 180 | ||